Many years ago I called 3m about this and was able to talk to a chemist and he told me that both 8115 and 8116 would release at 350 degrees. And if you look at the highlighted area down below, you can see where they performed strength tests. They did the tests at three different temperatures -40, 73, and 180 degrees. If you notice the failure psi was much higher at -40 degrees, and much lower at 180 degrees, as the adhesive gets softer with the higher temperature, and at 350 degrees in my own test it turned to dust. The adhesion test table is much easier to read in the link, it just wouldn't copy the same.
Also, as of May 2011 when I talked to the chemist he said that 8115 was the first one out and does not meet the car maker specs, if the 8116 fails it will be at the bond with the steel and any failure with 8115 will be the adhesive splitting.
http://multimedia.3m.com/mws/media/...a-sheet-3mtm-panel-bonding-adhesive-08115.pdf
Document Library
TS Data Sheet 08115
Public
Rev:3 Status: Active
Effective: 05/10/2006
3M(TM) Automix(TM) Panel Bonding Adhesive 8115
Data Sheet
Performance Properties
Overlap Shear Adhesion
Adhesion to Various Substrates
Typical overlap shear strength of bonds with 10 to 12 mil bondlines are reported below as pounds per
square inch (psi). All materials except aluminum, E-Coat, and two-part epoxy primed steel, were
abraded with a 50 grit coated abrasive and solvent wiped with 3M
™ General Purpose Adhesive Cleaner,
P.N. 08984. Aluminum samples were abraded with a Scotch-Brite
™ Rivet Cleaning Disc, P.N. 07410
and solvent wiped. E-Coat samples were solvent wiped. No extra surface preparation was performed
on the epoxy primed steel. The bonds were allowed to cure for 7 days at 73°F and then tested on a
Sintech tester at a joint separation rate of 0.5 inches/minute.
*all adhesion values in psi
Substrate -40°F 73°F 180°F
0.057" Steel/0.057" Steel 4003(C) 3935(C)*
0.036" Steel/0.036" Steel 3309(C) 2904(C) 1259(A)
0.035" E-Coat Primed Steel/0.035" E-Coat Primed Steel 3514(S)
0.036" Galvanized Steel/0.036" Galvanized Steel 3008(C)
Two-Part Epoxy Primed 0.036" Steel/Two-Part Epoxy Primed 0.036" Steel 2183
0.062" Aluminum 6111/0.062" Aluminum 6111 3144(C)
0.063" Aluminum 5754/0.063" Aluminum 5754 2152(A)
0.057" Steel/0.062" Aluminum 6111 3795(C)
FRP/FRP 1283(S)
SMC/SMC 785(S)
ABS (Acrylonitrile butadiene styrene)/ABS 942(S)
Acrylic (Plexiglas)/Acrylic 345(A)
Polycarbonate (Lexan)/Polycarbonate 733(S)
PVC/PVC 578(A)
HIPS (High Impact Polystyrene)/HIPS 122(A)
Polystyrene/Polystyrene 116(A)
Polypropylene/Polypropylene 435(A)
High Density Polyethylene/HDPE 311(A)
Low Density Polyethylene/LDPE 176(A)
SBR/SBR 104(S)
*(S)=Substrate Failure
(A)=Adhesive Failure
(C)=Cohesive Failure