Robbie mcmillian
What are your opinion about wet on wet sealers? Epoxy or 2k?
That was my thoughts.. I've done mostly production work for the last 20 years and epoxy is pretty slow. I was wondering if the color holdout would be any better with epoxy if time wasn't an issue.
If 50% reduction is added, does it stay n place pretty good or is it bad to sag/run?
I do have it all apart and thought about spraying it then putting it together . But I do know that can create a problem 2. Even if all the parts are sprayed at the same time.
You won't get better color holdout from an undercoat I think- it's the protection package in the clear that saves the colorYou do get better hold out with epoxy, if mixed 1:1:1 (50% reduction) is relatively fast as a sealer.
You won't get better color holdout from an undercoat I think- it's the protection package in the clear that saves the color